Comparisonal Analysis of Mechanical Properties on AISI 1095 Leaf Spring Steel With Steel Substitute Matrials Jis S45c and Jis Scm440
Abstract
Leaf springs are one of the components that function to soak the collision with the elastic properties of the material. where the leaf springs are made of steel materials such as AISI 1095 steel. In this study, a comparison of the mechanical properties of AISI 1095 leaf spring steels with S45C and SCM440 steels which are heat treated will be compared. Where the S45C material with a tempering temperature of 540°C obtains Yield Strength 555.6 MPa, and Ultimaate Strength 800.1 MPa, Hardness with an average of 69.3 HRA While at a temperature of 470°C obtains Yield Strength 561.3 MPa, and Ultimaate Strength 692.6 MPa, Hardness with an average of 71.5 HRA. For SCM440 having a tempering temperature of 540°C to get a Yield Strength of 829.8 MPa, and an Ultimaate Strength of 1053.7 MPa, Hardness with an average of 77.1 HRA While at a temperature of 470°C to obtain a Yield Strength of 846.4 MPa, and an Ultimaate Strength 1077.9 MPa, Hardness with an average of 70.7 HRA. From the results of this test, it is stated that the replacement material analyzed is close to the value of the SUP 10 steel spring.
Keywords
Full Text:
PDFReferences
A. B. Permana and A. M. Sakti, “Studi Eksperimen Kekuatan Impact dan Bending Baja Karbon Pegas Daun AISI 1095 Pada Mobil Kijang Kapsul 7K-EFI Tahun 2000 Dengan Perlakuan Panas Tempering,†JPTM Univ. Negeri Surabaya, vol. 09, no. 03, pp. 67–75, 2020.
T. Hidayat, “Analisa Kegagalan Pegas Daun (Leaf Spring) Pada Toyota Kijang Kapsul 7k-Ei Tahun 2000,†Univ. Muria Kudus, vol.2012.
R. Aditama, “Studi Eksperimen Kekuatan Tarik Dan Kekerasan Baja Karbon Pegas Daun Aisi 1095 Pada Mobil Kijang Kapsul 7k-Tahun 2000 Dengan Perlakuan Panas Tempering EFI Abstrak,â€Univ. Negeri Surabaya, vol. 07, no. 81, pp. 1–10.
M. Hudha, “Analisa Rekondisi Baja Pegas Daun Bekas Sup 9a Dengan Metode Quench-Temper Pada Temperatur Tempering 480°C Terhadap Kekerasan Dan Kekuatan Tarik,†Institut Teknologi Sepuluh Nopember Surabaya, 2017.
A. Rizky, “Pengaruh Variasi Media Pendingin Terhadap Kekerasan Baja Aisi 6135 Yang Mengalami Perlakuan Panas Anealing,†Universitas Muhammadiyah Sumatera Utara, 2020.
M. Nofri and T. Acang, “Analisis Sifat Mekanika Baja SKD 61 Dengan Baja ST 41 Dilakukan Hardening Dengan Variasi Temperatur,†Bina Tek., vol. 13, no. 2, pp. 189–199, 2017, [Online]. Available: https://ejournal.upnvj.ac.id/index.php/BinaTeknika/article/view/1322.
Setiawan, “Titik Terhadap Kekuatan Geser Las Titik ( Spot Welding ) Pada Baja ST 70,†fakultas teknik, 2007.
Z. Amin, “Pengujian Struktur Mikro Besi Pejal Baja St 60 Dengan Mikroskop Digital 16 Mp,†Politeknik Harapan Bersama Tegal, 2019.
J. T. Widdiyanto, “Analisa Sifat Mekanis Material Baja S45c Sebagai Pengganti Material Baja Aisi 1020 Untuk Komponen Sprocket Melalui Perlakuan Panas Analisa Sifat Mekanis Material Baja S45c Sebagai Pengganti Material Baja Aisi 1020 Untuk Komponen,†2021.
Tira Steel, PT. Tira Austenite Tbk. JAKARTA: PT. TIRA AUSTENITE, 2020.
J. Yuristianto, “Diagram Fasa Fe – Fe3C,†universitas brawijaya, 2012. https://blog.ub.ac.id/jefriyuristiant/2012/03/06/diagram-fasa-fe-fe3c/ (accessed Apr. 29, 2021).
Tira Steel, PT. Tira Austenite Tbk. JAKARTA: PT. TIRA AUSTENITE, 2020.
J. Yuristianto, “Diagram Fasa Fe – Fe3C,†universitas brawijaya, 2012. https://blog.ub.ac.id/jefriyuristiant/2012/03/06/diagram-fasa-fe-fe3c/ (accessed Apr. 29, 2021).
D. Mas, “Annealing Proses annealing,†pdfcoffee.com, 2016. https://pdfcoffee.com/11-12-perlakuan-panas-pdf-free.html#Dimas+Mas (accessed Apr. 29, 2021).
D. Nurjayanti and E. Ginting, “Pengaruh Lama Pemanasan , Pendinginan secara Cepat , dan Tempering 600 o C terhadap Sifat Ketangguhan pada Baja Pegas,†J. Teor. dan Apl. Fis., vol. 01, no. 02, pp. 113–120, 2013.
mochammad ghulam isaq Khan, “Tempering Terhadap Struktur Mikro Dan Sifat Mekanik Pada Baja Aar-M201,†Institut Teknologi Sepuluh November, 2015.
A. L. Khakim, “Pengaruh Variasi Media Pendingin Pada Sifat Mekanis Baja Karbon Rendah Untuk As Roda Sepeda Motor,†Universitas Pancasakti Tegal, 2020.
W. SAMPURNA, “Studi Eksperimen Proses Tempering Terhadap Kekerasan Permukaan Dan Estimasi Keausan,†Institut Teknologi Sepuluh Nopember, 2016.
Haryadi. Gunawan Dwi, “Pengaruh Suhu Tempering Terhadap Kekerasan , Kekuatan Tarik Dan Struktur Mikro Pada Baja K-460,†Tek. mesin FT-UNDIP, vol. 8, no. 5, pp. 1–8, 2006.
D. Juliaptini, “Skripsi Analisis Sifat Mekanik dan Metalografi Baja Karbon Rendah untuk Aplikasi Tabung Gas 3 Kg,†universitas islam negri syarif hidataullah, 2010.
L. Prabowo, “Pengaruh perlakuan kimia pada serat kelapa (Coir fiber),†universitas sanata dharma, 2007.
H. Budiman, “Analisis Pengujian Tarik (Tensile Test) Pada Baja St37 Dengan Alat Bantu Ukur Load Cell,†J-Ensitec, vol. 03, 2016.
A. Taufik, A. Suprapto, and A. A. ad Sonief, “Characteristic microstructure of micro hot rolled plate steel variating the radius of bending treatment with quenching and tempering heat treatment,†J. Appl. Eng. Sci., vol. 16, no. 4, pp. 464–470, 2018, doi: 10.5937/jaes16-18078.
FARIZAL, “Rancangan alat uji impak tipe charpy telah selesai dirancang sesuai dengan standar ASTM E 23 -02,†Universitas Teuku Umar Meulaboh, 2013.
Pengujian Material, Eko Budiyanto,Mt. Sulis Dri Handono,M,Eng CV.Laudy Alifatma April2020
Refbacks
- There are currently no refbacks.